News Details
The new coating USES crosslinking agent
2017-6-16 11:58:41
The new coating USES crosslinking agent
A steel structure pipe that is coated with a crosslinked thermoplastic elastomer. The elastomer is composed of 15 to 38 percent rubber, 62 ~ 85% of polypropylene resin, 10% of the curing agent, etc.
Will, for example, 20, 80 E150GK rubber, EPDM rubber 20 mica powder, 1.6 servings of crosslinking agent (contains SP1045, tin chloride and zinc oxide) at 220 ℃ under the condition of mixing extrusion, made a coating combination. The composite applies to steel structure pipe coating, which makes it have excellent heat resistance, low temperature resistance and so on.
A combination of radiation curing silicone coatings and their finishes. The coating compound contains:
(A) core-shell type tetragonal crystal system titanium oxide aqueous dispersions, which also contains the elements, such as tin, manganese and titanium and the ratio of the amount of substance of tin is 10/1 ~ 1000/1, titanium and the ratio of the amount of substance of manganese is 10/1 ~ 1000/1.
(B) polycarbonate and/or polyester carbamate modified ethylene polymers;
(C) hydrolyzed condensation, which is condensed by hydrolyzed by a non-sulfur-containing alkane silicane.
(D) light polymerization initiator
(E) solvent;
(F) colloidal silica; (G) unlike the polyethylene compounds of B and C. The patent also involves the coating process of coating the coating on the base material of organic resin, which can be coated directly without the need of the bottom coating. In addition, the coating is involved in the coating.
A two-component epoxy resin for the application of the surface of the steel structure. Prior to the construction of the coating, the two components need to be reactivated and pretreated with the surface of the steel.
Chinese name: Diethyl toluene diamine(DETDA)
Chinese alias: aryl, aryl diethyl - aryl - methyl-p-phenylenediamine
English name: Benzenediamine, ar, ar-diethyl-ar-methyl-English aliases:Diethyltoluenediamine; ar, ar-Diethyl-ar-methylbenzenediamine;Diethylmethylbenzenediamine;
CAS No. :68479-98-1
EINECS No. :270 -877-4
Molecular formula: C11H18N2
Molecular Weight: 178.28
Boiling point: 310 ℃
Refractive index: 1.581
Flash Point: > 140 ℃
Inchi: InChI = 1/C11H18N2/c1-4-8-6-7 (3) 10 (12) 11 (13) 9 (8) 5-2/h6H ,4-5,12-13H2 ,1-3H3 density : 1.022
Risk Codes: R10; R35
RIDADR: UN 3082
Safety instructions: S2; S26; S39; S61
Packing Group: III
Hazard Class: 6.1
The A component contains the components of low-viscosity glycosil aniline resin, hydroxycarboxylic acid accelerator, etc. The components of B component include the addition of amino-benzylaniline and polyethylene glycidyl ether. The two components contain the same amount of slip-on stuffing, which is a mixture of carbon fiber, molybdenum disulfide, ethyl acetate or butyl acetate.
An electronic component with multiple coating composite fire protection system. The multi-coating system consists of carbon base, first plasma polymer coating and second plasma polymer coating.
The polymer coating by phosphorus precursor or their mixture by plasma polymerization, another polymer coating by nitrogen precursor or their mixture by plasma polymerization. The multi-coating composite system is suitable for the expansion and non-halogen flame retardant system.
High temperature resistant coating and its preparation method. The patent covers a resistance to exposure of the base material surface treatment method, the base material is suitable for power plants and other industrial applications, can make the solar energy into other forms of energy such as heat or electricity.
The coating contains a particle whose thermal conductivity is greater than 3W/mK. The electromagnetic spectrum, according to research the topic of coating, the sunlight absorption rate is very high, and low emission rate, good high temperature resistance, good thermal conductivity, strong adhesion to metal substrate, good mechanical properties, high durability and corrosion resistence.
At present, it is mainly used to improve the surface performance of WPU coatings by using organic silicon and fluorine resin, and reduce the surface gibbs free energy. Yi xiang was used to synthesize the organic silicon modified epoxy-polyurethane emulsion with 3 per cent amino silane and 4 per cent epoxy resin. The emulsion was enhanced by the presence of the Si -o bond and the crosslinking of epoxy resin, which makes the coating surface hydrophobic and hydrophobic and resistant to water resistance.
Copyright: Zhang Jia Gang YaRui Chemical co.,Ltd
Diethyl toluene diamine(DETDA) http://www.yaruichem.com
A steel structure pipe that is coated with a crosslinked thermoplastic elastomer. The elastomer is composed of 15 to 38 percent rubber, 62 ~ 85% of polypropylene resin, 10% of the curing agent, etc.
Will, for example, 20, 80 E150GK rubber, EPDM rubber 20 mica powder, 1.6 servings of crosslinking agent (contains SP1045, tin chloride and zinc oxide) at 220 ℃ under the condition of mixing extrusion, made a coating combination. The composite applies to steel structure pipe coating, which makes it have excellent heat resistance, low temperature resistance and so on.
A combination of radiation curing silicone coatings and their finishes. The coating compound contains:
(A) core-shell type tetragonal crystal system titanium oxide aqueous dispersions, which also contains the elements, such as tin, manganese and titanium and the ratio of the amount of substance of tin is 10/1 ~ 1000/1, titanium and the ratio of the amount of substance of manganese is 10/1 ~ 1000/1.
(B) polycarbonate and/or polyester carbamate modified ethylene polymers;
(C) hydrolyzed condensation, which is condensed by hydrolyzed by a non-sulfur-containing alkane silicane.
(D) light polymerization initiator
(E) solvent;
(F) colloidal silica; (G) unlike the polyethylene compounds of B and C. The patent also involves the coating process of coating the coating on the base material of organic resin, which can be coated directly without the need of the bottom coating. In addition, the coating is involved in the coating.
A two-component epoxy resin for the application of the surface of the steel structure. Prior to the construction of the coating, the two components need to be reactivated and pretreated with the surface of the steel.
Chinese name: Diethyl toluene diamine(DETDA)
Chinese alias: aryl, aryl diethyl - aryl - methyl-p-phenylenediamine
English name: Benzenediamine, ar, ar-diethyl-ar-methyl-English aliases:Diethyltoluenediamine; ar, ar-Diethyl-ar-methylbenzenediamine;Diethylmethylbenzenediamine;
CAS No. :68479-98-1
EINECS No. :270 -877-4
Molecular formula: C11H18N2
Molecular Weight: 178.28
Boiling point: 310 ℃
Refractive index: 1.581
Flash Point: > 140 ℃
Inchi: InChI = 1/C11H18N2/c1-4-8-6-7 (3) 10 (12) 11 (13) 9 (8) 5-2/h6H ,4-5,12-13H2 ,1-3H3 density : 1.022
Risk Codes: R10; R35
RIDADR: UN 3082
Safety instructions: S2; S26; S39; S61
Packing Group: III
Hazard Class: 6.1
The A component contains the components of low-viscosity glycosil aniline resin, hydroxycarboxylic acid accelerator, etc. The components of B component include the addition of amino-benzylaniline and polyethylene glycidyl ether. The two components contain the same amount of slip-on stuffing, which is a mixture of carbon fiber, molybdenum disulfide, ethyl acetate or butyl acetate.
An electronic component with multiple coating composite fire protection system. The multi-coating system consists of carbon base, first plasma polymer coating and second plasma polymer coating.
The polymer coating by phosphorus precursor or their mixture by plasma polymerization, another polymer coating by nitrogen precursor or their mixture by plasma polymerization. The multi-coating composite system is suitable for the expansion and non-halogen flame retardant system.
High temperature resistant coating and its preparation method. The patent covers a resistance to exposure of the base material surface treatment method, the base material is suitable for power plants and other industrial applications, can make the solar energy into other forms of energy such as heat or electricity.
The coating contains a particle whose thermal conductivity is greater than 3W/mK. The electromagnetic spectrum, according to research the topic of coating, the sunlight absorption rate is very high, and low emission rate, good high temperature resistance, good thermal conductivity, strong adhesion to metal substrate, good mechanical properties, high durability and corrosion resistence.
At present, it is mainly used to improve the surface performance of WPU coatings by using organic silicon and fluorine resin, and reduce the surface gibbs free energy. Yi xiang was used to synthesize the organic silicon modified epoxy-polyurethane emulsion with 3 per cent amino silane and 4 per cent epoxy resin. The emulsion was enhanced by the presence of the Si -o bond and the crosslinking of epoxy resin, which makes the coating surface hydrophobic and hydrophobic and resistant to water resistance.
Copyright: Zhang Jia Gang YaRui Chemical co.,Ltd
Diethyl toluene diamine(DETDA) http://www.yaruichem.com
Spanish
French
Italian
Portuguese
Japanese
Korean
Arabic
Russian