Finish (paint) by crosslinking agent
2017-3-30 10:51:47
Finish (paint) by crosslinking agent,Deployment of paint.
Primer must be completely dry, metope can not have dust and other sundry.
Ratio of construction, the main paint, crosslinking agent, diluent = 10:1:2.
Allocate fluor-carbon painting must be used after the 200 mesh gauze filter, thinner in place should be constantly in the process of mixing, in order to avoid precipitation.
Spray gun models: W - 77, nozzle size: 1.5-2.0 mm, pump pressure: 0.3-0.5 Mp.
Construction should be considered when the number of spraying, spraying, spraying base area, the distribution of the hoisting cage, considering the actual situation of the project, arrange the construction personnel to spray at the same time, in guarantee under the premise of not sag, spray thicker as possible.
Should do a good job, antifouling and gas to drain pipe should be protected, such as gas masks and gloves should be worn when construction workers and other protective equipment, it is strictly prohibited to fireworks at the same time; Coating should be uniform, reasonable density, no flow uneven hang, light and shade, the phenomenon such as hair flower, feel is exquisite, burnish even, no batch of scraping marks and uneven phenomenon.
Compared with traditional paint coating, has better resistance to light, hou resistance;
Compared with the traditional external wall stick aluminum-plastic plate, operating more simple, renovation;
Cost much lower than the aluminum-plastic plate, and can achieve the same effect;
Quality is light, will not bring heavy burden to the wall, there is no risk of aluminum-plastic plate fall.
Steel surface: inorganic zinc-rich paint, epoxy or polyurethane primer
Plastic or glass fiber reinforced plastic: after surface treatment can be used directly.
The durability of the coating improve fluorocarbon resin emulsion and metal aluminium powder synthesized fluorocarbon metallic paint than ordinary silicon a crylic-acid or acrylic resin emulsion
Synthesis of metallic paint, in terms of durability (i.e., anti-aging performance) have greatly improved, is called "super durability of coating.
No need to paint layer of protection: because of the painting in acid and alkali resistance, resistance to ultraviolet radiation, weathering resistance, water resistance, antistatic performance of many parties
Chinese name: Diethyl toluene diamine(DETDA)
Diethyltoluenediamine Raw material ：
TDA industrial, Sichuan production
Ethylene (Et) polymer grade, Shanghai production
TEA industrial imports
A reagent grade additives
The improvement of the performance of the surface, so it has no need to use paint coating is, only after spraying the paint on craft can no longer paint application layer.
Metallic luster more prominent: the purpose of the metallic paint is to be with metallic luster, otherwise will lose its significance. Because the fluorine carbon paint the emulsion is transparent
More pure, more, so metal degrees are more likely to emerge.
Check the putty meets the requirements, there is problem timely repair.
In the metope of completely dry (wall to dry wall moisture content less than 8%) on spray primer (air pressure in the 5-8 kg/cm2, no water spraying).
Requires uniform spray, spray can't leak, should maintain uniform color, may not appear hair flower phenomenon, the wind can't construction (cet 6 or above) and rainy day.
Primer spraying again, check the spraying, found a batch of metope imprint or bee eye phenomenon, must be polished to conform to the requirements.
Polished 280 mesh and 360 mesh should be adopted for the water sand paper, burnish carefully, pay attention to the coating can not be worn through.
Should carry on the dust removal process the burnish, use towels to clean grinding of dust on metope processing. If the dust is not complete, fluorocarbon lacquer after construction will not be able to achieve a smooth film.
After the primer coating, should be uniform color, luster evenly, coating surface is smooth, no dust and stain.
Copyright: Zhang Jia Gang YaRui Chemical co.,Ltd
Diethyl toluene diamine(DETDA) http://www.yaruichem.com
Primer must be completely dry, metope can not have dust and other sundry.
Ratio of construction, the main paint, crosslinking agent, diluent = 10:1:2.
Allocate fluor-carbon painting must be used after the 200 mesh gauze filter, thinner in place should be constantly in the process of mixing, in order to avoid precipitation.
Spray gun models: W - 77, nozzle size: 1.5-2.0 mm, pump pressure: 0.3-0.5 Mp.
Construction should be considered when the number of spraying, spraying, spraying base area, the distribution of the hoisting cage, considering the actual situation of the project, arrange the construction personnel to spray at the same time, in guarantee under the premise of not sag, spray thicker as possible.
Should do a good job, antifouling and gas to drain pipe should be protected, such as gas masks and gloves should be worn when construction workers and other protective equipment, it is strictly prohibited to fireworks at the same time; Coating should be uniform, reasonable density, no flow uneven hang, light and shade, the phenomenon such as hair flower, feel is exquisite, burnish even, no batch of scraping marks and uneven phenomenon.
Compared with traditional paint coating, has better resistance to light, hou resistance;
Compared with the traditional external wall stick aluminum-plastic plate, operating more simple, renovation;
Cost much lower than the aluminum-plastic plate, and can achieve the same effect;
Quality is light, will not bring heavy burden to the wall, there is no risk of aluminum-plastic plate fall.
Steel surface: inorganic zinc-rich paint, epoxy or polyurethane primer
Plastic or glass fiber reinforced plastic: after surface treatment can be used directly.
The durability of the coating improve fluorocarbon resin emulsion and metal aluminium powder synthesized fluorocarbon metallic paint than ordinary silicon a crylic-acid or acrylic resin emulsion
Synthesis of metallic paint, in terms of durability (i.e., anti-aging performance) have greatly improved, is called "super durability of coating.
No need to paint layer of protection: because of the painting in acid and alkali resistance, resistance to ultraviolet radiation, weathering resistance, water resistance, antistatic performance of many parties
Chinese name: Diethyl toluene diamine(DETDA)
Diethyltoluenediamine Raw material ：
TDA industrial, Sichuan production
Ethylene (Et) polymer grade, Shanghai production
TEA industrial imports
A reagent grade additives
The improvement of the performance of the surface, so it has no need to use paint coating is, only after spraying the paint on craft can no longer paint application layer.
Metallic luster more prominent: the purpose of the metallic paint is to be with metallic luster, otherwise will lose its significance. Because the fluorine carbon paint the emulsion is transparent
More pure, more, so metal degrees are more likely to emerge.
Check the putty meets the requirements, there is problem timely repair.
In the metope of completely dry (wall to dry wall moisture content less than 8%) on spray primer (air pressure in the 5-8 kg/cm2, no water spraying).
Requires uniform spray, spray can't leak, should maintain uniform color, may not appear hair flower phenomenon, the wind can't construction (cet 6 or above) and rainy day.
Primer spraying again, check the spraying, found a batch of metope imprint or bee eye phenomenon, must be polished to conform to the requirements.
Polished 280 mesh and 360 mesh should be adopted for the water sand paper, burnish carefully, pay attention to the coating can not be worn through.
Should carry on the dust removal process the burnish, use towels to clean grinding of dust on metope processing. If the dust is not complete, fluorocarbon lacquer after construction will not be able to achieve a smooth film.
After the primer coating, should be uniform color, luster evenly, coating surface is smooth, no dust and stain.