Amide amine coating crosslinking agent
2017-3-4 23:35:04
Amide amine coating crosslinking agent, amide amine is polyamine and fatty acid addition polymerization reaction. The characteristics of both aliphatic amine and polyamide. Amide amine with fatty amine rapid crosslinking, good water resistance and corrosion resistance, and is similar to the polyamide longer operational time and good flexibility. Amide amine smaller molecular weight to ensure that the product of low viscosity, while ensuring a longer operating time, at the same time, the late crosslinked with the shear strength) of the (hardness, time is short.
Amide amine main characteristics are as follows:
1. Low viscosity, convenient operation
2. Good intermiscibility with resin
3. The longer operational time, room temperature with 1-3 hours of operation time (200 g, 25 ℃)
4. Short crosslinking time, 1.5 4.5 hours of crosslinking temperature (25 ℃), 200 g.
5. Wet to united in the absence of MingShui MBB league in good condition
6. The lower heating temperature, the heating temperature is generally lower than 65 ℃ (200 g, 25 ℃)
7. Crosslinking with excellent physical properties, high tensile, compressive, flexural and shear properties.
8. Crosslinking with excellent resistance to water, the performance of the acid and alkali resistance and other chemicals.
9. Excellent adhesion
10. Excellent gloss
11. Good flexibility
Based on its superior wet to united, amide amine epoxy coating can be used to produce low surface treatment.
Polyamide resin, it is the excellent performance of widely used chemical raw materials, according to its nature can be divided into two broad categories: non reactive or neutral polyamide and reactive polyamides. Neutral polyamide mainly for the production of printing ink, heat sealing adhesive and coating, reactive polyamide curing agent for epoxy resin, and used for thermosetting surface coating, adhesive, lining material and tank sealing, molded resin.
Chinese name: Diethyl toluene diamine(DETDA)
Physical and chemical properties: light yellow transparent liquid, slightly soluble in water, soluble in alcohols, ethers, ketones and other polar organic solvents, and polyether, polyester polyol compatibility.
Density 1.022
Viscosity (20 ℃) ??mPa·ss290±10
Pour Point ℃-9
Boiling point of310°C
Flash Point°C161.1°C
Polyamide resin, it is the excellent performance of widely used chemical raw materials, according to its nature can be divided into two broad categories: non reactive or neutral polyamide and reactive polyamides. Neutral polyamide mainly for the production of printing ink, heat sealing adhesive and coating, reactive polyamide curing agent for epoxy resin, and used for thermosetting surface coating, adhesive, lining material and tank sealing, molded resin.
Neutral dimer acid polyamide resin adhesive on polyethylene substrates such as well, particularly suitable for packaging film on surface of the polyethylene, printed on the foil laminated film and other plastic film; Neutral polyamide resin ink gloss, good bonding performance, good diluted alcohol resistance, low gelling property, quick drying, little smell.
Dimer acid base of thermal bonding resin, widely used in shoemaking, cans, packaging and bookbinding; Used in seam sealed cans packaging; For apples, oranges and other frozen fruit juice the adhesive of the new structure of the container. MWCNTS polyamide adhesive, due to the dry cleaning resistance, resistance to strong detergent, bleach and conditions of high temperature washing, laundry room and family for fabric strong adhesive united strength is convenient to use and used for objects stick couplet; Because has the necessary cohesive force and good resistance to wet and used for heat shrinkable cable sets.
Other USES of neutral polyamine resin including preparation of thixotropic coating, water-based glue, fabric antistatic agent, transparent candle and detergent.
Further reaction reactivity polyamide resin and used as curing agent of epoxy resin, have broad crosslinked thermosetting resin. When used as a curing agent, has a pair of optional the gender is big, non-toxic, can be room temperature curing, and the advantages of soft not brittle, can make the epoxy resin has excellent caking property, flexural toughness, chemical resistance, resistance to wet and smooth surface.
Copyright: Zhang Jia Gang YaRui Chemical co.,Ltd
Amide amine main characteristics are as follows:
1. Low viscosity, convenient operation
2. Good intermiscibility with resin
3. The longer operational time, room temperature with 1-3 hours of operation time (200 g, 25 ℃)
4. Short crosslinking time, 1.5 4.5 hours of crosslinking temperature (25 ℃), 200 g.
5. Wet to united in the absence of MingShui MBB league in good condition
6. The lower heating temperature, the heating temperature is generally lower than 65 ℃ (200 g, 25 ℃)
7. Crosslinking with excellent physical properties, high tensile, compressive, flexural and shear properties.
8. Crosslinking with excellent resistance to water, the performance of the acid and alkali resistance and other chemicals.
9. Excellent adhesion
10. Excellent gloss
11. Good flexibility
Based on its superior wet to united, amide amine epoxy coating can be used to produce low surface treatment.
Polyamide resin, it is the excellent performance of widely used chemical raw materials, according to its nature can be divided into two broad categories: non reactive or neutral polyamide and reactive polyamides. Neutral polyamide mainly for the production of printing ink, heat sealing adhesive and coating, reactive polyamide curing agent for epoxy resin, and used for thermosetting surface coating, adhesive, lining material and tank sealing, molded resin.
Chinese name: Diethyl toluene diamine(DETDA)
Physical and chemical properties: light yellow transparent liquid, slightly soluble in water, soluble in alcohols, ethers, ketones and other polar organic solvents, and polyether, polyester polyol compatibility.
Density 1.022
Viscosity (20 ℃) ??mPa·ss290±10
Pour Point ℃-9
Boiling point of310°C
Flash Point°C161.1°C
Polyamide resin, it is the excellent performance of widely used chemical raw materials, according to its nature can be divided into two broad categories: non reactive or neutral polyamide and reactive polyamides. Neutral polyamide mainly for the production of printing ink, heat sealing adhesive and coating, reactive polyamide curing agent for epoxy resin, and used for thermosetting surface coating, adhesive, lining material and tank sealing, molded resin.
Neutral dimer acid polyamide resin adhesive on polyethylene substrates such as well, particularly suitable for packaging film on surface of the polyethylene, printed on the foil laminated film and other plastic film; Neutral polyamide resin ink gloss, good bonding performance, good diluted alcohol resistance, low gelling property, quick drying, little smell.
Dimer acid base of thermal bonding resin, widely used in shoemaking, cans, packaging and bookbinding; Used in seam sealed cans packaging; For apples, oranges and other frozen fruit juice the adhesive of the new structure of the container. MWCNTS polyamide adhesive, due to the dry cleaning resistance, resistance to strong detergent, bleach and conditions of high temperature washing, laundry room and family for fabric strong adhesive united strength is convenient to use and used for objects stick couplet; Because has the necessary cohesive force and good resistance to wet and used for heat shrinkable cable sets.
Other USES of neutral polyamine resin including preparation of thixotropic coating, water-based glue, fabric antistatic agent, transparent candle and detergent.
Further reaction reactivity polyamide resin and used as curing agent of epoxy resin, have broad crosslinked thermosetting resin. When used as a curing agent, has a pair of optional the gender is big, non-toxic, can be room temperature curing, and the advantages of soft not brittle, can make the epoxy resin has excellent caking property, flexural toughness, chemical resistance, resistance to wet and smooth surface.